QUESTION 8ELECTROCHEMISTRY: Copper was electroplated from a Cu2SO4 solution onto an electrode with an active surface area of 7.55 cm. Determine the thickness (mm) of the3deposit if the current is kept constant at 4.61 A for 0.9284 hours. (density of Cu = 8.96 g/cm, MW of Cu = 63.55 g/mol). (Input values only with 2 decimal places. Do notinclude the unit.)

Answered: Image /qna-images/answer/47f624d3-ba56-4823-8bff-8774d765420b.jpg

QUESTION 8 ELECTROCHEMISTRY: Copper was electroplated from a Cu2SO4 solution onto an electrode with an active surface area of 7.55 cm. Determine the thickness (mm) of the deposit if the current is kept constant at 4.61 A for 0.9284 hours. (density of Cu = 8.96 g/cm, MVW of Cu = 63.55 g/mol). (Input values only with 2 decimal places. Do not include the unit)

QUESTION 8 ELECTROCHEMISTRY: Copper was electroplated from a Cu2SO4 solution onto an electrode with an active surface area of 7.55 cm. Determine the thickness (mm) of the deposit if the current is kept constant at 4.61 A for 0.9284 hours. (density of Cu = 8.96 g/cm, MVW of Cu = 63.55 g/mol). (Input values only with 2 decimal places. Do not include the unit)

Chemistry: The Molecular Science

5th Edition

ISBN:9781285199047

Author:John W. Moore, Conrad L. Stanitski

Publisher:John W. Moore, Conrad L. Stanitski

Chapter17: Electrochemistry And Its Applications

Section: Chapter Questions

Problem 89QRT: You wish to electroplate a copper surface having an area of 1200 mm2 with a 1.0-m-thick coating of...

See similar textbooks

Similar questions

How long would it take to electroplate a metal surface with 0.500 g nickel metal from a solution of Ni2+ with a current of 4.00 A?
A metallurgist wants to gold-plate an object with a surface area of 17.21 in2. The gold plating must be 0.00200 in. thick (assume uniform thickness). (a) How many grams of gold (d=10.5g/cm3) are required? (b) How many minutes will it take to plate the object from a solution of AuCN using a current of 7.00 A? Assume 100% efficiency.
Repeat the directions for Question 106 using a cell constructed of a strip of nickel immersed in a 1.0-M Ni2+ solution and a strip of silver dipping into a 1.0-M Ag+ solution. Write the balanced chemical equation for the reaction that is product-favored. Calculate the cell potential. Draw a sketch of the cell and indicate the anode, cathode, and direction of electron flow.
An alloy made up of tin and copper is prepared by simultaneously electroplating the two metals from a solution containing Sn(NO3)2 and Cu(NO3)2.If 20.0% of the total current is used to plate tin, while 80.0% is used to plate copper, what is the percent composition of the alloy?
What volume of F2 gas, at 25C and 1.00 atm, is produced when molten KF is electrolyzed by a current of 10.0 A for 2.00 h? What mass of potassium metal is produced? At which electrode does each reaction occur?
You wish to electroplate a copper surface having an area of 1200 mm2 with a 1.0-m-thick coating of silver froma solution of Ag(CN)2 ions. If you use a current of150.0 mA, calculate how much electrolysis time youshould use. The density of metallic silver is 10.5 g/cm3.
An aqueous solution of an unknown salt of gold is electrolyzed by a current of 2.75 amps for 3.39 hours. The electroplating is carried out with an efficiency of 93.0%, resulting in a deposit of 21.221 g of gold. a How many faradays are required to deposit the gold? b What is the charge on the gold ions (based on your calculations)?
In the electrolysis of a solution containing Ag+(aq), metallic Ag(s) deposits on the cathode. Using a current of 1.12 A for 2.40 hours, what mass of silver forms?