7.8 Design the concrete mix according to the following conditions:Design EnvironmentBuilding frameRequired design strengthMinimum dimension27.6 MPa||150 mmMinimum space between rebarMinimum cover over rebarStatistical data indicate a standard deviation of compressive strength of2.1 MPa is expected (more than 30 samples).Only air entrainer is allowed.40 mm= 40 mmAvailable MaterialsAir entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement.Coarse aggregate: 19 mm nominal maximum size, river gravel(rounded)Bulk oven-dry specific gravityOven-dry rodded densityMoisture content = 2.5%2.55, Absorption= 0.3%= 1761 kg/m³Fine aggregate: Natural sandBulk oven-dry specific gravity2.659, Absorption0.5%Moisture content =2%Fineness modulus2.47%3D

Calculate required strength Assume S = 2.1 Mpa Calculate the value of fcrfcr = fc + 1.34S= 30.4…

7.8 Design the concrete mix according to the following conditions: Design Environment Building frame Required design strength Minimum dimension = 27.6 MPa = 150 mm Minimum space between rebar Minimum cover over rebar = 40 mm = 40 mm Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples). Only air entrainer is allowed. Available Materials Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement.

7.8 Design the concrete mix according to the following conditions: Design Environment Building frame Required design strength Minimum dimension = 27.6 MPa = 150 mm Minimum space between rebar Minimum cover over rebar = 40 mm = 40 mm Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples). Only air entrainer is allowed. Available Materials Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

7.8 Design the concrete mix according to the following conditions: Design Environment Building frame Required design strength = 27.6 MPa Minimum dimension = 150 mm Minimum space between rebar = 40 mm Minimum cover over rebar = 40 mm Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples). Only air entrainer is allowed. Available Materials Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement. Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded) Bulk oven-dry specific gravity = 2.55, absorption = 3.6% Oven-dry rodded density = 1761 kg/m³ Moisture content = 2.5% Fine aggregate: Natural sand Bulk oven-dry specific gravity Moisture content = 2% Fineness modulus = 2.47 = 2.659, absorption = 0.5%
Q3: B: Design the concrete mix according to the following conditions: Design Environment Building frame Required design strength = 27.6 MPa Minimum dimension = 150 mm Minimum space between rebar = 40 mm Minimum cover over rebar = 40 mm Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples). Only air entrainer is allowed. Available Materials Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement. Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded) Bulk oven-dry specific gravity = 2.55, absorption = 3.6, Oven-dry rodded density = 1761 kg/m3 %3D Moisture content = 2.5, Fine aggregate: Natural sand Bulk oven-dry specific gravity 2.659, absorption=0.5, Moisture content = 2, Fineness modulus = 2.47
Design the concrete mix according to the following conditions:Design Environment• Building beamo Required design strength = 27.6 MPao Minimum dimension = 150 mmo Minimum space between rebar = 40 mmo Minimum cover over rebar = 40 mmo Statistical data indicate a standard deviation of compressive strengthof 2.1 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Moderate Sulphate exposure.• Available Materialso Air entrainer:▪ Manufacture specification 6.3 mL/1% air/100 kg cement.o Coarse aggregate:▪ 19 mm nominal maximum size▪ River gravel (rounded)▪ Bulk oven-dry specific gravity = 2.55▪ Absorption = 3.6▪ Oven-dry rodded density = 1761 kg/m3▪ Moisture content = 2.5o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.659▪ Absorption = 0.5▪ Moisture content = 2▪ Fineness modulus = 2.47o Cement▪ Type II (Moderate Sulphate Resistant)▪ Specific Gravity = 3.15Based on this information, find the following and summarize the findings in a table.a) Required…
Design the concrete mix according to the following conditions:Design Environment• Concrete slabo Subjected to freeze and thaw.o Required design strength = 21 MPao Slab thickness = 300 mm.o Statistical data indicate a standard deviation of compressive strengthof 1.7 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Available Materials:o Air entrainer:▪ Manufacture specification is 9.5 mL/1% air/100 kg cement.o Coarse aggregate:▪ 25 mm nominal maximum size▪ Crushed stone▪ Bulk oven-dry specific gravity = 2.573▪ Absorption = 2.8▪ Oven-dry rodded density = 1922 kg/m3▪ Moisture content = 1o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.540▪ Absorption = 3.4▪ Moisture content = 4.5▪ Fineness modulus = 2.60o Cement:▪ Type I Cement▪ Specific gravity = 3.15…
Design the concrete mix according to the following conditions:Design Environment• Building beamo Required design strength = 27.6 MPao Minimum dimension = 150 mmo Minimum space between rebar = 40 mmo Minimum cover over rebar = 40 mmo Statistical data indicate a standard deviation of compressive strengthof 2.1 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Moderate Sulphate exposure.• Available Materialso Air entrainer:▪ Manufacture specification 6.3 mL/1% air/100 kg cement.o Coarse aggregate:▪ 19 mm nominal maximum size▪ River gravel (rounded)▪ Bulk oven-dry specific gravity = 2.55▪ Absorption = 3.6▪ Oven-dry rodded density = 1761 kg/m3▪ Moisture content = 2.5o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.659▪ Absorption = 0.5▪ Moisture content = 2▪ Fineness modulus = 2.47o Cement▪ Type II (Moderate Sulphate Resistant)▪ Specific Gravity = 3.15Based on this information, find the following and summarize the findings in a table d) The amount…
Design the concrete mix according to the following conditions:Design Environment• Concrete slabo Subjected to freeze and thaw.o Required design strength = 21 MPao Slab thickness = 300 mm.o Statistical data indicate a standard deviation of compressive strengthof 1.7 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Available Materials:o Air entrainer:▪ Manufacture specification is 9.5 mL/1% air/100 kg cement.o Coarse aggregate:▪ 25 mm nominal maximum size▪ Crushed stone▪ Bulk oven-dry specific gravity = 2.573▪ Absorption = 2.8▪ Oven-dry rodded density = 1922 kg/m3▪ Moisture content = 1o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.540▪ Absorption = 3.4▪ Moisture content = 4.5▪ Fineness modulus = 2.60o Cement:▪ Type I Cement▪ Specific gravity = 3.15Find the required quantities of cement, water, coarse aggregate, fine aggregate, aircontent, and admixture per 1 m3 of concrete. Summarize the findings in a table.Based on this information, find the…
Design a concrete mix for the following conditions and constraints using the absolute volume method:Design EnvironmentBuilding frameRequired design strength = 27.6 MPaMinimum dimension = 150 mmMinimum space between rebars = 40 mmMinimum cover over rebars = 40 mmStatistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples)Only air entrainer is allowedAvailable MaterialsAir EntrainerManufacturer specification 6.3 ml/1% air / 100 kg cementCoarse aggregate19 mm nominal maximum size, river gravel (rounded)Bulk oven dry specific gravity = 2.55, Absorption = 0.3%Oven dry-rodded density = 1761 kg/m3Moisture content = 2.5%Fine aggregateNatural sandBulk oven-dry specific gravity = 2.659, Absorption = 0.5%Moisture content = 2%Fineness modulus = 2.47
Design the concrete mix according to the following conditions: Design Environment Building frame Required design strength = 27.6 MPa Minimum dimension = 150 mm Minimum space between rebar = 40 mm Minimum cover over rebar = 40 mm Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples). Only air entrainer is allowed. Available Materials Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement. Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded) Bulk oven-dry specific gravity = 2.55, Absorption = 0.3% Oven-dry rodded density = 1761 kg/m3 Moisture content = 2% Fineness modulus = 2.47
Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, subjected to freezingRequired design strength = 21 MPaSlab thickness = 300 mmStatistical data indicate a standard deviation of compressive strength of1.7 MPa is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 9.5 mL/1% air/100 kgcement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 1922 kg/m3Moisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68
What is your recommendation for the maximum size of coarse aggregate for the following situation? A reinforce concrete column with the cross-section showed in figure below have the dimensions of 300*300 mm and the clear space between reinforcement and form of 50 mm. The minimum clear space between reinforcement is 180 mm. -180 mm 150 mm 300 mm
Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, Bozeman, Montana (cold climate)Required design strength = 3000 psiSlab thickness = 12 in.Statistical data indicate a standard deviation of compressive strength of250 psi is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 0.15 fl oz/1% air/100 lb cement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 120 pcfMoisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68
10. Design a concrete mix for the following conditions and constraints using the absolute volume method Design Environment Bridge pier exposed to freezing and subjected to deicing chemicals Required design = 25.1 MPa Minimum dimension = 0.4 m Minimum space between rebars = 60 mm Minimum cover over rebars = 50 mm Standard deviation of compressive strength of 2.8 MPa is expected (more than 30 samples) Only air entrainer is allowed Available Materials Cement Select Type V due to exposure Air Entrainer Manufacturer specification 6.2 ml/1% air/100 kg cement Coarse aggregate 25 mm maximum size, river gravel (round) Bulk oven dry specific gravity = 2.621, Absorption = 0.4% Oven dry-rodded density = 1650 kg/m3 Moisture content = 1.4% Fine aggregate Natural sand Bulk oven-dry specific gravity = 2.576, Absorption = 0.7% Moisture content = 3% Fineness modulus = 2.50