3. A concrete mix includes the following ingredients per cubic foot: (14 pts.) Cement 25 Ibs. Water I1 Ibs. No Admixture Table shows possible changes that can be made to the mix ingredients. Indicate in the appropriate boxes in the table what will happen in each case for the workability and the ultimate compressive strength as increase, decrease, or approximately the same. What WIIII Happen? Ultimate Compressive Strength Cement (Ib) Water (Ib) Admixture Workability 25 15 None 28 11 None 25 11 Water reducer Water reducer Superplasticizer 25 8. 25 11 25 11 Air entrainer 25 11 Accelerator

3. A concrete mix includes the following ingredients per cubic foot: (14 pts.) Cement 25 Ibs. Water I1 Ibs. No Admixture Table shows possible changes that can be made to the mix ingredients. Indicate in the appropriate boxes in the table what will happen in each case for the workability and the ultimate compressive strength as increase, decrease, or approximately the same. What WIIII Happen? Ultimate Compressive Strength Cement (Ib) Water (Ib) Admixture Workability 25 15 None 28 11 None 25 11 Water reducer Water reducer Superplasticizer 25 8. 25 11 25 11 Air entrainer 25 11 Accelerator

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Design the concrete mix according to the following conditions:Design Environment• Concrete slabo Subjected to freeze and thaw.o Required design strength = 21 MPao Slab thickness = 300 mm.o Statistical data indicate a standard deviation of compressive strengthof 1.7 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Available Materials:o Air entrainer:▪ Manufacture specification is 9.5 mL/1% air/100 kg cement.o Coarse aggregate:▪ 25 mm nominal maximum size▪ Crushed stone▪ Bulk oven-dry specific gravity = 2.573▪ Absorption = 2.8▪ Oven-dry rodded density = 1922 kg/m3▪ Moisture content = 1o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.540▪ Absorption = 3.4▪ Moisture content = 4.5▪ Fineness modulus = 2.60o Cement:▪ Type I Cement▪ Specific gravity = 3.15…
Design the concrete mix according to the following conditions:Design EnvironmentBuilding frameRequired design strength = 27.6 MPaMinimum dimension = 150 mmMinimum space between rebar = 40 mmMinimum cover over rebar = 40 mmStatistical data indicate a standard deviation of compressive strength of2.1 MPa is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification 6.3 mL/1% air/100 kg cement.Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded)Bulk oven-dry specific gravity = 2.55, absorption = 3.6,Oven-dry rodded density = 1761 kg/m3Moisture content = 2.5,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.659, absorption = 0.5,Moisture content = 2,Fineness modulus = 2.47
A concrete mix includes the following ingredients per cubic meter: Cement%3D400 kg Water=184 kg No admixture Table below shows possible alternatives mix ingredients. Indicate in the appropriate boxes in the table what will happen in each case for the workability and the ultimate compressive strength as increase, decrease or approximately the same. What will happen? Cement Water Admixture (kg) (kg) Ultimate compressive Workability strength 400 225 None 449 184 None Water 400 184 Reducer Water 400 128 Reducer 400 184 Super Plasticizer 400 184 Air Entrainer 400 184 Accelerator DFocus
Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, subjected to freezingRequired design strength = 21 MPaSlab thickness = 300 mmStatistical data indicate a standard deviation of compressive strength of1.7 MPa is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 9.5 mL/1% air/100 kgcement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 1922 kg/m3Moisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68
Design the concrete mix according to the following conditions:Design Environment• Concrete slabo Subjected to freeze and thaw.o Required design strength = 21 MPao Slab thickness = 300 mm.o Statistical data indicate a standard deviation of compressive strengthof 1.7 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Available Materials:o Air entrainer:▪ Manufacture specification is 9.5 mL/1% air/100 kg cement.o Coarse aggregate:▪ 25 mm nominal maximum size▪ Crushed stone▪ Bulk oven-dry specific gravity = 2.573▪ Absorption = 2.8▪ Oven-dry rodded density = 1922 kg/m3▪ Moisture content = 1o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.540▪ Absorption = 3.4▪ Moisture content = 4.5▪ Fineness modulus = 2.60o Cement:▪ Type I Cement▪ Specific gravity = 3.15Find the required quantities of cement, water, coarse aggregate, fine aggregate, aircontent, and admixture per 1 m3 of concrete. Summarize the findings in a table.Based on this information, find the…
a) Calculate the temperature of aggregates to produce fresh concrete having the sametemperature with the ambient temperature. Following data in Table 1 could be used:
The design engineer specifies a concrete strength of 3700 psi. A plant where s = 300 psi for 41 test results. Which is the required average compressive strength to be used in your mix design? a. 3900 psi; b) 4000 psi; c)4 100 psi; d) 4200 psi
Problem 2: If f = 3 ksi what is the modulus of elasticity Ec and the maximum tensile stress fr that the concrete can carry before cracking (use ACI recommended equations). Assume a unit weight of the plain concrete is: a. Wc = 90- b. w lb lb 118- ft39 ft3) C. W = 160- Problem 3: Wight 3-6 Rugblom 4: Wight ? 7 lb ft3
Design the concrete mix according to the following conditions:Design Environment• Building beamo Required design strength = 27.6 MPao Minimum dimension = 150 mmo Minimum space between rebar = 40 mmo Minimum cover over rebar = 40 mmo Statistical data indicate a standard deviation of compressive strengthof 2.1 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Moderate Sulphate exposure.• Available Materialso Air entrainer:▪ Manufacture specification 6.3 mL/1% air/100 kg cement.o Coarse aggregate:▪ 19 mm nominal maximum size▪ River gravel (rounded)▪ Bulk oven-dry specific gravity = 2.55▪ Absorption = 3.6▪ Oven-dry rodded density = 1761 kg/m3▪ Moisture content = 2.5o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.659▪ Absorption = 0.5▪ Moisture content = 2▪ Fineness modulus = 2.47o Cement▪ Type II (Moderate Sulphate Resistant)▪ Specific Gravity = 3.15Based on this information, find the following and summarize the findings in a table.a) Required…
0 ww C. 6.31 A concrete mix includes the following ingredients per cubic foot: a. Cement = 25 lb b. Water = 11 lb c. No admixture Table P6.31 shows possible changes that can be made to the mix ingredi- ents. Indicate in the appropriate boxes in the table what will happen in each case for the workability and the ultimate compressive strength as increase, decrease, or approximately the same. TABLE P6.31 to dignope Cement (lb) 25 28 25 25 25 25 25 amigur Water (lb) 15 11 11 8 11 11 11 Admixture None None Water reducer Water reducer Superplasticizer Air entrainer Accelerator What Will Happen? www.10345 Ultimate Compressive we Strength Workability
Q3: B: Design the concrete mix according to the following conditions: Design Environment Building frame Required design strength = 27.6 MPa Minimum dimension = 150 mm Minimum space between rebar = 40 mm Minimum cover over rebar = 40 mm Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples). Only air entrainer is allowed. Available Materials Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement. Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded) Bulk oven-dry specific gravity = 2.55, absorption = 3.6, Oven-dry rodded density = 1761 kg/m3 %3D Moisture content = 2.5, Fine aggregate: Natural sand Bulk oven-dry specific gravity 2.659, absorption=0.5, Moisture content = 2, Fineness modulus = 2.47
Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, Bozeman, Montana (cold climate)Required design strength = 3000 psiSlab thickness = 12 in.Statistical data indicate a standard deviation of compressive strength of250 psi is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 0.15 fl oz/1% air/100 lb cement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 120 pcfMoisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68